Overview

The deformation process observed in the hot gas side wall of rocket combustion chambers was investigaged for three different liner materials. Five thrust chambers were cycled to failure by using hydrogen and oxygen as propellants at a chamber pressure of 4.14 MN/cu m. The deformation was observed nondestructively at midlife points and destructively after failure occurred. The cyclic life results are presented with an accompanying discussion about the problems of life prediction associated with the types of failures encountered in the present work. Data indicating the deformation of the thrust chamber liner as cycles are accumulated are presented for each of the test thrust chambers. From these deformation data and observation of the failure sites it is evident that modeling the failure process as classic low cycle thermal fatigue is inadequate as a life prediction method. Hannum, N. P. and Price, R. G., Jr. Glenn Research Center NASA-TP-1834, E-553 RTOP 506-52-12

Full Product Details

9781724710031

Table of Contents

Reviews

Author Information

Tab Content 6

Countries Available