Overview

In 1996, Marshall Space Flight Center developed a multistep heating rate-controlled (MSRC) aging technique that significantly enhanced cryogenic fracture toughness (CFT) and reduced the statistical spread of fracture toughness values in alloy 2195 by controlling the location and size of strengthening precipitate T1. However, it could not be readily applied to flight-related hardware production, primarily because large-scale production furnaces are unable to maintain a heating rate of 0.6 C (1 F)/hr. In August 1996, a new program was initiated to determine whether the MSRC aging treatment could be further modified to facilitate its implementation to flight hardware production. It was successfully redesigned into a simplified two-step aging treatment consisting of 132 C (270 F)/20 hr + 138 C (280 F)/40 hr. Results indicated that two-step aging can achieve the same yield strength levels as those produced by conventional aging while providing greatly improved ductility. Two-step aging proved to be very effective at enhancing CFT, enabling previously rejected materials to meet simulated service requirements. Cryogenic properties are improved by controlling T1 nucleation and growth so that they are promoted in the matrix and suppressed in the subgrain boundaries.Chen, P. S. and Stanton, W. P.Marshall Space Flight CenterFRACTURE STRENGTH; AGING (METALLURGY); HEAT TREATMENT; PRECIPITATION HARDENING; ALUMINUM-LITHIUM ALLOYS; COPPER ALLOYS; PRECIPITATES; YIELD STRENGTH; NUCLEATION; PROPELLANT TANKS...

Full Product Details

9781726213363

Table of Contents

Reviews

Author Information

Tab Content 6

Countries Available