OverviewThe corrosion behavior of austenitic and superaustenitic stainless steels was investigated in carbon dioxide-saturated synthetic oil field formation water using cyclic polarization tests. In order to measure the effect of carbon dioxide pressure, the samples were also exposed in a pressurized medium containing carbon dioxide and synthetic air. For this purpose, tests were performed for long exposure time at 80 DegreesC under 8 MPa of a mixture of carbon dioxide and synthetic air both acting together. The results indicated that the type of corrosion on the surfaces of the samples after all the tests was pitting corrosion. According to the results, the AL-6XNPLUS(TM) steel presented the best performance in all experiments. The results also indicated that the conventional austenitic stainless steels are not suitable for the use in carbon dioxide containing environment in aqueous medium. Full Product DetailsAuthor: Marcel Mandel , Lutz Kruger , Luis Flavio Gaspar HerculanoPublisher: Eliva Press Imprint: Eliva Press Dimensions: Width: 15.20cm , Height: 0.20cm , Length: 22.90cm Weight: 0.068kg ISBN: 9781636480619ISBN 10: 1636480616 Pages: 40 Publication Date: 17 December 2020 Audience: General/trade , General Format: Paperback Publisher's Status: Active Availability: In stock We have confirmation that this item is in stock with the supplier. It will be ordered in for you and dispatched immediately. Table of ContentsReviewsAuthor InformationTab Content 6Author Website:Countries AvailableAll regions |